Fondinox > 2RE60

2RE60

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
- - 1.4417 S31500 - AISI 329
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 18.5 4.9 2.8 - -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
410 650 25 200-260 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenoferritic 7.75 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent - 2.3
Categoria: Sandvik
ACI/CAST
GRADE
-
CAST ASTM -
CAST EN/DIN 1.4417
CAST UNS S31500
WROUGHT
UNS
-
WROUGHT
GRADE
AISI 329
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 18.5
Ni 4.9
Mo 2.8
Other -
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 410
Rm [MPa] 650
A % 25
Hardness [HB] 200-260
Impact [J] 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenoferritic
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining -
Patternmaker’s Shrinkage [%] 2.3