Fondinox > 353MA®

353MA®

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
- - 1.4854 X6NiCrSiNCe35-25 - S35315 353MA®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.20 25.0 35.0 - Ce, N -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
260 500 15 - -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, Carbides 7.9 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
As Cast - - 2.6
Categoria: Outokumpu Oy
ACI/CAST
GRADE
-
CAST ASTM -
CAST EN/DIN 1.4854 X6NiCrSiNCe35-25
CAST UNS -
WROUGHT
UNS
S35315
WROUGHT
GRADE
353MA®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.20
Cr 25.0
Ni 35.0
Mo -
Other Ce, N
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 260
Rm [MPa] 500
A % 15
Hardness [HB] -
Impact [J] -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, Carbides
ρ [kg/dm3] 7.9
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment As Cast
Weldability -
Machining -
Patternmaker’s Shrinkage [%] 2.6