Fondinox > ALLOY 25/5LC®

ALLOY 25/5LC®

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
ALLOY 25/5LC - - - - -
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 25.0 7.0 2.5 0.12N -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
450 640 20 200-280 90
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenoferritic 7.75 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Escellent - 2.3
Categoria: Duplex/Superduplex
ACI/CAST
GRADE
ALLOY 25/5LC
CAST ASTM -
CAST EN/DIN -
CAST UNS -
WROUGHT
UNS
-
WROUGHT
GRADE
-
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 25.0
Ni 7.0
Mo 2.5
Other 0.12N
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 450
Rm [MPa] 640
A % 20
Hardness [HB] 200-280
Impact [J] 90
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenoferritic
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Escellent
Machining -
Patternmaker’s Shrinkage [%] 2.3