Fondinox > C2000C

C2000C

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
C2000C - - - - Hastelloy C2000®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 23.0 Bal. 16.2 Fe<3.0, 1.6Cu -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
275 550 25 160-230 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.5 12.4 9.1 428 1328-1358
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 44 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
C2000C
CAST ASTM -
CAST EN/DIN -
CAST UNS -
WROUGHT
UNS
-
WROUGHT
GRADE
Hastelloy C2000®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 23.0
Ni Bal.
Mo 16.2
Other Fe<3.0, 1.6Cu
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 275
Rm [MPa] 550
A % 25
Hardness [HB] 160-230
Impact [J] 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.5
α [μm/m∙K] (20 - 100 °C) 12.4
K [W/m∙K] 9.1
Cp [J/kg∙K] 428
Melting ΔT [°C] 1328-1358
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining 44
Patternmaker’s Shrinkage [%] 1.8