Fondinox > CA15

CA15

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CA15 A743, A487, A217 1.4008 GX8CrNi13 J91150 S41000 AISI 410
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
0,10 12,5 <1.0 <0.5
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
450 620 18 170-240 40
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Martensitic 7,61 10.5 30 460 1510
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Quenched and Tempered Satisfactory 110 2.0%
Categoria: Martensitic
ACI/CAST
GRADE
CA15
CAST ASTM A743, A487, A217
CAST EN/DIN 1.4008 GX8CrNi13
CAST UNS J91150
WROUGHT
UNS
S41000
WROUGHT
GRADE
AISI 410
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C 0,10
Cr 12,5
Ni <1.0
Mo <0.5
Other
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 450
Rm [MPa] 620
A % 18
Hardness [HB] 170-240
Impact [J] 40
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Martensitic
ρ [kg/dm3] 7,61
α [μm/m∙K] (20 - 100 °C) 10.5
K [W/m∙K] 30
Cp [J/kg∙K] 460
Melting ΔT [°C] 1510
WORKING CONDITIONS / FABRICATION
Heat Treatment Quenched and Tempered
Weldability Satisfactory
Machining 110
Patternmaker’s Shrinkage [%] 2.0%