Fondinox > CD6MN

CD6MN

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CD6MN, 3A A890, A995 - J93371 - AISI 329
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.08 25.0 5.5 2.0 0.2N -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
450 655 25 200-280 80
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenoferritic 7.75 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
SOlution Annealing Satisfactory - 2.3
Categoria: Duplex/Superduplex
ACI/CAST
GRADE
CD6MN, 3A
CAST ASTM A890, A995
CAST EN/DIN -
CAST UNS J93371
WROUGHT
UNS
-
WROUGHT
GRADE
AISI 329
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.08
Cr 25.0
Ni 5.5
Mo 2.0
Other 0.2N
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 450
Rm [MPa] 655
A % 25
Hardness [HB] 200-280
Impact [J] 80
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenoferritic
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment SOlution Annealing
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 2.3