Fondinox > CF10SMNN

CF10SMNN

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CF10SMNN A351, A743 - - - NITRONIC 60®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.10 17.0 8.5 - N0.14
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
295 585 30 140-220 80
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 7.75 15.8 - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Acceptable with precautions 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CF10SMNN
CAST ASTM A351, A743
CAST EN/DIN -
CAST UNS -
WROUGHT
UNS
-
WROUGHT
GRADE
NITRONIC 60®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.10
Cr 17.0
Ni 8.5
Mo -
Other N0.14
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 295
Rm [MPa] 585
A % 30
Hardness [HB] 140-220
Impact [J] 80
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) 15.8
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Acceptable with precautions
Machining
Patternmaker’s Shrinkage [%] 2.6