Fondinox > CF16F

CF16F

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CF16F A743 - J92701 - AISI 303
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.16 19.5 10.5 <1.5 S, (P), (Se)
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
205 485 30 140-200 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic (δ ferrite, Intermetallics) 7.75 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Satisfactory 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CF16F
CAST ASTM A743
CAST EN/DIN -
CAST UNS J92701
WROUGHT
UNS
-
WROUGHT
GRADE
AISI 303
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.16
Cr 19.5
Ni 10.5
Mo <1.5
Other S, (P), (Se)
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 205
Rm [MPa] 485
A % 30
Hardness [HB] 140-200
Impact [J] 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic (δ ferrite, Intermetallics)
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Satisfactory
Machining
Patternmaker’s Shrinkage [%] 2.6