Fondinox > CF3

CF3

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CF3 A351, A743, A744 1.4306 X2CrNi19-11 J92500 S30403 AISI 304L
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 19.0 10.0 <0.5 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
205 485 35 140-200 140
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic (δ ferrite) 7.75 16 15 500 -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CF3
CAST ASTM A351, A743, A744
CAST EN/DIN 1.4306 X2CrNi19-11
CAST UNS J92500
WROUGHT
UNS
S30403
WROUGHT
GRADE
AISI 304L
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 19.0
Ni 10.0
Mo <0.5
Other -
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 205
Rm [MPa] 485
A % 35
Hardness [HB] 140-200
Impact [J] 140
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic (δ ferrite)
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) 16
K [W/m∙K] 15
Cp [J/kg∙K] 500
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining
Patternmaker’s Shrinkage [%] 2.6