Fondinox > CF3MN

CF3MN

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CF3MN A351 - J92804 S31653 AISI 316LN
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 18.0 10.0 2.3 N0.15
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
255 515 35 150-200 140
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 7.75 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CF3MN
CAST ASTM A351
CAST EN/DIN -
CAST UNS J92804
WROUGHT
UNS
S31653
WROUGHT
GRADE
AISI 316LN
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 18.0
Ni 10.0
Mo 2.3
Other N0.15
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 255
Rm [MPa] 515
A % 35
Hardness [HB] 150-200
Impact [J] 140
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining
Patternmaker’s Shrinkage [%] 2.6