CF8M

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CF8M A351, A743, A744 1.4408 GX6CrNiMo18-10 J92900 S31600 AISI 316
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.08 18.5 10.0 2.3 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
205 485 30 140-200 120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic (δ ferrite) 7.75 16 24 445 1302-1451
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealed Excellent 100 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CF8M
CAST ASTM A351, A743, A744
CAST EN/DIN 1.4408 GX6CrNiMo18-10
CAST UNS J92900
WROUGHT
UNS
S31600
WROUGHT
GRADE
AISI 316
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.08
Cr 18.5
Ni 10.0
Mo 2.3
Other -
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 205
Rm [MPa] 485
A % 30
Hardness [HB] 140-200
Impact [J] 120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic (δ ferrite)
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) 16
K [W/m∙K] 24
Cp [J/kg∙K] 445
Melting ΔT [°C] 1302-1451
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealed
Weldability Excellent
Machining 100
Patternmaker’s Shrinkage [%] 2.6