Fondinox > CG3M

CG3M

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CG3M A351, A743, A744 - J92999 S31702 AISI 317L
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 19.5 10.0 3.3 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
240 515 25 150-200 110
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (δ ferrite) 7.75 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CG3M
CAST ASTM A351, A743, A744
CAST EN/DIN -
CAST UNS J92999
WROUGHT
UNS
S31702
WROUGHT
GRADE
AISI 317L
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 19.5
Ni 10.0
Mo 3.3
Other -
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 240
Rm [MPa] 515
A % 25
Hardness [HB] 150-200
Impact [J] 110
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (δ ferrite)
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining
Patternmaker’s Shrinkage [%] 2.6