Fondinox > CW2M

CW2M

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CW2M A494 2.4610 NiMo16Cr16Ti N26455 N06455 Hastelloy C4®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 16.0 Bal. 16.0 Fe<2.0, W<1.0 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
275 495 25 160-230 120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.64 10.8 10.1 406 -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 44 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
CW2M
CAST ASTM A494
CAST EN/DIN 2.4610 NiMo16Cr16Ti
CAST UNS N26455
WROUGHT
UNS
N06455
WROUGHT
GRADE
Hastelloy C4®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 16.0
Ni Bal.
Mo 16.0
Other Fe<2.0, W<1.0
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 275
Rm [MPa] 495
A % 25
Hardness [HB] 160-230
Impact [J] 120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.64
α [μm/m∙K] (20 - 100 °C) 10.8
K [W/m∙K] 10.1
Cp [J/kg∙K] 406
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining 44
Patternmaker’s Shrinkage [%] 1.8