Fondinox > CX2M

CX2M

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CX2M A494 2.4607 GNiCr23Mo16 N26059 - ALLOY 59
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 23.0 Bal. 15.5 Fe<1.5 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
270 495 40 160-230 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.70 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
CX2M
CAST ASTM A494
CAST EN/DIN 2.4607 GNiCr23Mo16
CAST UNS N26059
WROUGHT
UNS
-
WROUGHT
GRADE
ALLOY 59
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 23.0
Ni Bal.
Mo 15.5
Other Fe<1.5
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 270
Rm [MPa] 495
A % 40
Hardness [HB] 160-230
Impact [J] 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.70
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining
Patternmaker’s Shrinkage [%] 1.8