Fondinox > CX2MW

CX2MW

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CX2MW A494 9.4602 N26022 N06022 Hastelloy C22®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 21.5 Bal. 13.5 Fe<6.0, 3.0W, V<0.35
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
270 495 40 160-230 110
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.69 12.4 10.1 414 1357-1399
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 44 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
CX2MW
CAST ASTM A494
CAST EN/DIN 9.4602
CAST UNS N26022
WROUGHT
UNS
N06022
WROUGHT
GRADE
Hastelloy C22®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 21.5
Ni Bal.
Mo 13.5
Other Fe<6.0, 3.0W, V<0.35
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 270
Rm [MPa] 495
A % 40
Hardness [HB] 160-230
Impact [J] 110
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.69
α [μm/m∙K] (20 - 100 °C) 12.4
K [W/m∙K] 10.1
Cp [J/kg∙K] 414
Melting ΔT [°C] 1357-1399
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining 44
Patternmaker’s Shrinkage [%] 1.8