Fondinox > CY40

CY40

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CY40 A494 2.4816 NiCr15Fe N06040 N06600 INCONEL 600
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.4 15.5 Bal. - Fe<11.0, Si<3.0 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
195 485 30 160-270 60
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Carbides) 8.35 - - - 1354-1413
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Annealing, Solution Annealing Satisfactory - 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
CY40
CAST ASTM A494
CAST EN/DIN 2.4816 NiCr15Fe
CAST UNS N06040
WROUGHT
UNS
N06600
WROUGHT
GRADE
INCONEL 600
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.4
Cr 15.5
Ni Bal.
Mo -
Other Fe<11.0, Si<3.0
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 195
Rm [MPa] 485
A % 30
Hardness [HB] 160-270
Impact [J] 60
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Carbides)
ρ [kg/dm3] 8.35
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] 1354-1413
WORKING CONDITIONS / FABRICATION
Heat Treatment Annealing, Solution Annealing
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 1.8