Fondinox > CY40

CY40

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CY40 A494 - N06040 - INCONEL 600
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Si Other
0.1 15.0 Bal. 1.8 8.0Fe
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
195 485 30 - -
CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C Creep strength for 100.000 hours MPa at °C
600 700 800 900 1000 1100 600 700 800 900 1000 1100
- 60 41 21 7 2 - 48 28 15 7 2
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, Carbides 8.47 10.4 14.9 444 1353-1413
WORKING CONDITIONS / FABRICATION
Heat Treatment Max working T in air [°C] Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
As Cast 1100 - 2.2
Categoria: Nickel and Cobalt Base
ACI/CAST
GRADE
CY40
CAST ASTM A494
CAST EN/DIN -
CAST UNS N06040
WROUGHT
UNS
-
WROUGHT
GRADE
INCONEL 600
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C 0.1
Cr 15.0
Ni Bal.
Si 1.8
Other 8.0Fe
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 195
Rm [MPa] 485
A % 30
Hardness [HB] -
Impact [J] -
CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C
600 -
700 60
800 41
900 21
1000 7
1100 2
Creep strength for 100.000 hours MPa at °C
600 -
700 48
800 28
900 15
1000 7
1100 2
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, Carbides
ρ [kg/dm3] 8.47
α [μm/m∙K] (20 - 100 °C) 10.4
K [W/m∙K] 14.9
Cp [J/kg∙K] 444
Melting ΔT [°C] 1353-1413
WORKING CONDITIONS / FABRICATION
Heat Treatment As Cast
Max working T in air [°C] 1100
Machining -
Patternmaker’s Shrinkage [%] 2.2