Fondinox > CZ100

CZ100

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CZ100 A494 2.4066 N02100 N02100 NICKEL 200
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<1.0 - Bal. - Fe<3.0 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
125 345 10 100-160 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Carbides) 8.34 13.3 70.3 456 1435-1446
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Annealed Satisfactory 100 2.0
Categoria: Nickel Base
ACI/CAST
GRADE
CZ100
CAST ASTM A494
CAST EN/DIN 2.4066
CAST UNS N02100
WROUGHT
UNS
N02100
WROUGHT
GRADE
NICKEL 200
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <1.0
Cr -
Ni Bal.
Mo -
Other Fe<3.0
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 125
Rm [MPa] 345
A % 10
Hardness [HB] 100-160
Impact [J] 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Carbides)
ρ [kg/dm3] 8.34
α [μm/m∙K] (20 - 100 °C) 13.3
K [W/m∙K] 70.3
Cp [J/kg∙K] 456
Melting ΔT [°C] 1435-1446
WORKING CONDITIONS / FABRICATION
Heat Treatment Annealed
Weldability Satisfactory
Machining 100
Patternmaker’s Shrinkage [%] 2.0