Fondinox > G35C

G35C

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
G35C - 2.4643 NiCr33Mo8 N06035 - Hastelloy G35®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 33.4 Bal. 8.3 Fe<2.0, W<0.6 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
305 565 35 180 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.22 12.3 10 450 1332-1361
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Satisfactory - 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
G35C
CAST ASTM -
CAST EN/DIN 2.4643 NiCr33Mo8
CAST UNS N06035
WROUGHT
UNS
-
WROUGHT
GRADE
Hastelloy G35®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 33.4
Ni Bal.
Mo 8.3
Other Fe<2.0, W<0.6
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 305
Rm [MPa] 565
A % 35
Hardness [HB] 180
Impact [J] 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.22
α [μm/m∙K] (20 - 100 °C) 12.3
K [W/m∙K] 10
Cp [J/kg∙K] 450
Melting ΔT [°C] 1332-1361
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 1.8