Fondinox > HASTELLOY C22®

HASTELLOY C22®

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CX2MW A494 9.4602 - N26022 HASTELLOY C22®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 21.5 Bal. 13.5 Fe<6.0, 3.0W, V<0.35 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
310 550 30 160-230 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.69 12.4 10.1 414 1357-1399
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Escellent - 1.8
Categoria: Haynes Intl.
ACI/CAST
GRADE
CX2MW
CAST ASTM A494
CAST EN/DIN 9.4602
CAST UNS -
WROUGHT
UNS
N26022
WROUGHT
GRADE
HASTELLOY C22®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 21.5
Ni Bal.
Mo 13.5
Other Fe<6.0, 3.0W, V<0.35
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 310
Rm [MPa] 550
A % 30
Hardness [HB] 160-230
Impact [J] 100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.69
α [μm/m∙K] (20 - 100 °C) 12.4
K [W/m∙K] 10.1
Cp [J/kg∙K] 414
Melting ΔT [°C] 1357-1399
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Escellent
Machining -
Patternmaker’s Shrinkage [%] 1.8