Fondinox > HASTELLOY C22HS®

HASTELLOY C22HS®

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
- - - - - HASTELLOY C22HS®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 20.7 bAL. 16.5 Fe<1.8
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
430 720 18 220-280 50
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.6 11.6 11.8 412 1304-1368
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution annealing, Aging Satisfactory - 1.8
Categoria: Haynes Intl.
ACI/CAST
GRADE
-
CAST ASTM -
CAST EN/DIN -
CAST UNS -
WROUGHT
UNS
-
WROUGHT
GRADE
HASTELLOY C22HS®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 20.7
Ni bAL.
Mo 16.5
Other Fe<1.8
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 430
Rm [MPa] 720
A % 18
Hardness [HB] 220-280
Impact [J] 50
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.6
α [μm/m∙K] (20 - 100 °C) 11.6
K [W/m∙K] 11.8
Cp [J/kg∙K] 412
Melting ΔT [°C] 1304-1368
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution annealing, Aging
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 1.8