Fondinox > HASTELLOY C276

HASTELLOY C276

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CW-12MW A494 2.4686 GNiMo17Cr N30002 N10276 HASTELLOY C276
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.12 16.5 Bal. 17.0 Fe<7.5, 4.25W, 0.30V
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
275 495 4 160-240 50
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.89 11.2 10.2 427 1323-1371
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Satisfactory - 1.8
Categoria: Haynes Intl.
ACI/CAST
GRADE
CW-12MW
CAST ASTM A494
CAST EN/DIN 2.4686 GNiMo17Cr
CAST UNS N30002
WROUGHT
UNS
N10276
WROUGHT
GRADE
HASTELLOY C276
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.12
Cr 16.5
Ni Bal.
Mo 17.0
Other Fe<7.5, 4.25W, 0.30V
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 275
Rm [MPa] 495
A % 4
Hardness [HB] 160-240
Impact [J] 50
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.89
α [μm/m∙K] (20 - 100 °C) 11.2
K [W/m∙K] 10.2
Cp [J/kg∙K] 427
Melting ΔT [°C] 1323-1371
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 1.8