Fondinox > HASTELLOY HYBRID BC1®

HASTELLOY HYBRID BC1®

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
- - - - N10362 HASTELLOY HYBRID BC1®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.02 15.0 Bal. 22.0 Fe<2.0 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
360 620 30 160 -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.83 11.5 9.3 402 -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing - 44 1.8
Categoria: Haynes Intl.
ACI/CAST
GRADE
-
CAST ASTM -
CAST EN/DIN -
CAST UNS -
WROUGHT
UNS
N10362
WROUGHT
GRADE
HASTELLOY HYBRID BC1®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.02
Cr 15.0
Ni Bal.
Mo 22.0
Other Fe<2.0
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 360
Rm [MPa] 620
A % 30
Hardness [HB] 160
Impact [J] -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.83
α [μm/m∙K] (20 - 100 °C) 11.5
K [W/m∙K] 9.3
Cp [J/kg∙K] 402
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability -
Machining 44
Patternmaker’s Shrinkage [%] 1.8