Fondinox > M30C

M30C

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
M30C A494 2.4365 GNiCu30Nb N24130 - -
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.3 - Bal. - 30.0Cu, Fe<3.5, 1.5Si, 2.0Nb -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
225 450 25 - -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 8.36 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Annealing Satisfactory - 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
M30C
CAST ASTM A494
CAST EN/DIN 2.4365 GNiCu30Nb
CAST UNS N24130
WROUGHT
UNS
-
WROUGHT
GRADE
-
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.3
Cr -
Ni Bal.
Mo -
Other 30.0Cu, Fe<3.5, 1.5Si, 2.0Nb
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 225
Rm [MPa] 450
A % 25
Hardness [HB] -
Impact [J] -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 8.36
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Annealing
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 1.8