Fondinox > M30H

M30H

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
M30H A494 2.4367 GNiCu30Si3 N24030 N05500 MONEL 500
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.3 - Bal. - 30.0Cu, Fe<3.5, 3.2Si
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
415 690 10 230-300 -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic, (Intermetallics) 8.45 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Annealing, (Precipitation Hardening) Acceptable with Precautions 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
M30H
CAST ASTM A494
CAST EN/DIN 2.4367 GNiCu30Si3
CAST UNS N24030
WROUGHT
UNS
N05500
WROUGHT
GRADE
MONEL 500
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.3
Cr -
Ni Bal.
Mo -
Other 30.0Cu, Fe<3.5, 3.2Si
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 415
Rm [MPa] 690
A % 10
Hardness [HB] 230-300
Impact [J] -
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic, (Intermetallics)
ρ [kg/dm3] 8.45
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Annealing, (Precipitation Hardening)
Weldability Acceptable with Precautions
Machining
Patternmaker’s Shrinkage [%] 1.8

Fondinox S.p.A © - All rights reserved