Fondinox > M35-1

M35-1

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
M35-1 A494 2.4360 NiCu30Fe N24135 N04400 Monel 400
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.35 - Bal. - 29.0Cu, Fe<3.5, Nb<0.5 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
170 450 25 100-160 80
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 8.63 14.2 22 427 1300-1350
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Annealing Excellent - 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
M35-1
CAST ASTM A494
CAST EN/DIN 2.4360 NiCu30Fe
CAST UNS N24135
WROUGHT
UNS
N04400
WROUGHT
GRADE
Monel 400
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.35
Cr -
Ni Bal.
Mo -
Other 29.0Cu, Fe<3.5, Nb<0.5
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 170
Rm [MPa] 450
A % 25
Hardness [HB] 100-160
Impact [J] 80
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 8.63
α [μm/m∙K] (20 - 100 °C) 14.2
K [W/m∙K] 22
Cp [J/kg∙K] 427
Melting ΔT [°C] 1300-1350
WORKING CONDITIONS / FABRICATION
Heat Treatment Annealing
Weldability Excellent
Machining -
Patternmaker’s Shrinkage [%] 1.8