Fondinox > M35-2

M35-2

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
M35-2 A494 - N24020 - -
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.35 - Bal. - 29.0Cu, Fe<3.5, Nb<0.5 -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
205 450 25 140-200 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 8.63 - - - -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Annealing Excellent - 1.8
Categoria: Nickel Base
ACI/CAST
GRADE
M35-2
CAST ASTM A494
CAST EN/DIN -
CAST UNS N24020
WROUGHT
UNS
-
WROUGHT
GRADE
-
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.35
Cr -
Ni Bal.
Mo -
Other 29.0Cu, Fe<3.5, Nb<0.5
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 205
Rm [MPa] 450
A % 25
Hardness [HB] 140-200
Impact [J] 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 8.63
α [μm/m∙K] (20 - 100 °C) -
K [W/m∙K] -
Cp [J/kg∙K] -
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Annealing
Weldability Excellent
Machining -
Patternmaker’s Shrinkage [%] 1.8