Fondinox > S34565

S34565

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
S34565 - 1.4565 - S34565 -
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 24.0 18.0 4.5 0.45N, 5.5Mn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
340 600 35 160-220 140
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 8.0 14.5 12 450 -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent - 2.6
Categoria: Superaustenitic
ACI/CAST
GRADE
S34565
CAST ASTM -
CAST EN/DIN 1.4565
CAST UNS -
WROUGHT
UNS
S34565
WROUGHT
GRADE
-
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 24.0
Ni 18.0
Mo 4.5
Other 0.45N, 5.5Mn
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 340
Rm [MPa] 600
A % 35
Hardness [HB] 160-220
Impact [J] 140
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 8.0
α [μm/m∙K] (20 - 100 °C) 14.5
K [W/m∙K] 12
Cp [J/kg∙K] 450
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining -
Patternmaker’s Shrinkage [%] 2.6