Fondinox > SANICRO 28®

SANICRO 28®

ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
- - 1.4563 X1NiCrMoCuN31-27-4 - N08028 SANICRO 28®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 27.0 31.0 3.5 1.0Cu -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
200 460 30 140-200 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 - 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 8.0 15 10 460 -
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Satisfactory - 2.8
Categoria: Sandvik
ACI/CAST
GRADE
-
CAST ASTM -
CAST EN/DIN 1.4563 X1NiCrMoCuN31-27-4
CAST UNS -
WROUGHT
UNS
N08028
WROUGHT
GRADE
SANICRO 28®
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 27.0
Ni 31.0
Mo 3.5
Other 1.0Cu
PREn -
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 200
Rm [MPa] 460
A % 30
Hardness [HB] 140-200
Impact [J] 70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 8.0
α [μm/m∙K] (20 - 100 °C) 15
K [W/m∙K] 10
Cp [J/kg∙K] 460
Melting ΔT [°C] -
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Satisfactory
Machining -
Patternmaker’s Shrinkage [%] 2.8